涂料工业  2018, Vol. 48 Issue (1): 1-5
  探索开发 |
张国梁, 马春风*, 张广照
华南理工大学材料科学与工程学院,广州 510640
Study on Permeable Coating for Anticorrosion of Concrete
Zhang Guoliang, Ma Chunfeng, Zhang Guangzhao
Faculty of Materials Science and Engineering, South China University of Technology, Guangzhou 510640, China
下载:  PDF (1706KB) 
输出:  BibTeX | EndNote (RIS)      
摘要 混凝土具有多孔结构,水和离子可通过混凝土的孔隙渗入于混凝土内部,对混凝土造成腐蚀。以环氧树脂和糠醛/丙酮制备了渗入固结型混凝土防腐涂料 (PSEp),其中糠醛/丙酮混合物为反应性溶剂。制得的涂料具有优异的润湿性能,能够渗入砂浆固结体(水灰比为0.5)的孔隙中并原位交联 (渗入深度可达4.0 mm),从而对混凝土孔隙进行封闭。该涂料渗入混凝土后与之形成复合增强层,其粘附力(拉拔强度)比混凝土提高130%。同时,混凝土表面抗离子渗入能力提高,其电通量从3 400 C下降至130 C。因此,该涂料可有效用于混凝土防腐。
E-mail Alert
关键词:  混凝土防腐  渗入固结  环氧树脂  反应性溶剂    
Abstract: The concrete has a porous structure. It suffers from deterioration caused by permeation of ions and water. In this article, a permeable coating (PSEp) for concrete has been prepared by using epoxy and furfural acetone. The coating has excellent wettability on concrete surface. Specifically, it can permeate into the pores or defects of mortar (W/C=0.5) with its depth up to 4.0 mm and cures thereat so that the concrete surface can be sealed. The mechanical property of the concrete is significantly improved by coating PSEp. The adhesion (pull-off strength) of the coated concrete is increased by more than 130%. Moreover, the resistance to ion permeability of the coated concrete increases, and the total electric flux decreases from 3 400 C to 130 C. The coating (PSEp) is useful for anticorrosion of concrete.
Key words:  concrete anticorrosion    permeation    epoxy    reactive solvent
收稿日期:  2017-11-14                出版日期:  2018-01-01      发布日期:  2018-05-03      期的出版日期:  2018-01-01
ZTFLH:  TQ 635.2  
作者简介:  张国梁(1990—),男,博士,主要从事重防腐涂料的开发与研究。
张国梁, 马春风, 张广照. 渗入固结型混凝土防腐涂料的研究[J]. 涂料工业, 2018, 48(1): 1-5.
Zhang Guoliang, Ma Chunfeng, Zhang Guangzhao. Study on Permeable Coating for Anticorrosion of Concrete. Paint & Coatings Industry, 2018, 48(1): 1-5.
链接本文:  或
[1] BASHEER L, KROPP J, CLELAND D J. Assessment of the durability of concrete from its permeation properties: a review[J]. Construction and Building Materials, 2001, 15 (2-3):93-103.<br />
[2] FLORES-VIVIAN I, HEJAZI V, KOZHUKHOVA M I, et al. Self-assembling particle-siloxane coatings for superhydrophobic concrete[J]. ACS Applied Materials & Interfaces, 2013, 5(24):13284-13294.<br />
[3] HANŽICˇ L, ILIC' R. Relationship between liquid sorptivity and capillarity in concrete[J]. Cement and Concrete Research, 2003, 33(9):1385-1388.<br />
[4] SØRENSEN P A, KIIL S, DAM-JOHANSEN K, et al. Anticorrosive coatings: a review[J]. Journal of Coatings Technology and Research, 2009, 6(2): 135-176.<br />
[5] BASHEER P A M, BASHEER L, CLELAND D J, et al. Surface treatments for concrete: assessmentmethods and reported performance[J]. Construction and Building Materials, 1997, 11(7-8): 413-429.<br />
[6] PIENS M, DE DEURWAERDER H. Effect of coating stress on adherence and on corrosion prevention[J]. Progress in Organic Coatings, 2001, 43(1): 18-24.<br />
[7] 张广照, 何泳生, 洗安如, 等. 环氧-糠醛-丙酮类化学灌浆材料中的糠醛-丙酮反应[J]. 岩土工程学报, 1995, 17(2): 47-52.<br />
[8] ZHU Y, KOU S, POON C, et al. Influence of silane-based water repellent on the durability properties of recycled aggregate concrete[J]. Cement and Concrete Composites, 2013,35(1):32-38.<br />
[9] MEDEIROS M H F, HELENE P. Surface treatment of reinforced concrete in marine environment: influence on chloride diffusion coefficient and capillary water absorption[J]. Construction and Building Materials, 2009, 23(3):1476-1484.<br />
[10] YE G, LURA P, VAN BREUGEL K. Modelling of water permeability in cementitious materials[J]. Materials and Structures, 2006, 39(9):877-885.<br />
[11] NOWAK E, COMBES G, STITT E H, et al. A comparison of contact angle measurement techniques applied to highly porous catalyst supports[J]. Powder Technology, 2013, 233:52-64.<br />
[12] KIIL S. Mathematical modelling of simultaneous solvent evaporation and chemical curing in thermoset coatings: a parameter study[J]. Progress in Organic Coatings, 2011, 70(4):192-198.<br />
[13] NEWMAN D J, NUNN C J. Solvent retention in organic coatings[J]. Progress in Organic Coatings, 1975, 3(3):221-243.
[1] 翁亶 秦真波 周潼 刘磊 胡文彬. 硅溶胶对无机磷酸铝涂料防腐性能的影响[J]. , 2018, 48(5): 7-013.
[2] 李自军, 刘胜林, 耿刚强. 聚苯胺微乳液的制备及其在水性醇酸涂料中的应用[J]. 涂料工业, 2018, 48(1): 11-16.
[1] Luo Ping, Liu Zhaohui, Yang Hongbo, Shu Xin, Tao Rui, Zhang Yanan. Effect of Fusion Temperature on Properties of Al-SiC Silicate-Based Ceramic Coating[J]. Paint & Coatings Industry, 2018, 48(1): 6 -10 .
[2] Li Zijun, Liu Shenglin, Geng Gangqiang. Preparation of Polyaniline Microemulsion and Its Application in Waterborne Alkyd Coatings[J]. Paint & Coatings Industry, 2018, 48(1): 11 -16 .
[3] Wang Liuyang, Ye Mengxing, Wang Shan, Liu Fangfang. Preparation and Properties of Polyurethane/Urea Modified by Phenolic Resin[J]. Paint & Coatings Industry, 2018, 48(1): 17 -21 .
[4] Su Guohui, Tang Ying, Cai Wei. Preparation and Performance of Waterborne Sand-Containing Multicolor Coatings[J]. Paint & Coatings Industry, 2018, 48(1): 22 -27 .
[5] Li Yu, Wang Guoqing, Wan Yi, Ding Chunhua, Wang Aimin. Preparation of Silicone Oil Microcapsules with Bionic Antifouling Performance[J]. Paint & Coatings Industry, 2018, 48(1): 28 -36 .
[6] Li Yongyue, Yan Kun, Ma Jinghong, Gong Jinghua. Preparation of Low Friction Polyurethane Composite Coating by Blending[J]. Paint & Coatings Industry, 2018, 48(1): 37 -43 .
[7] Yuan Quan, Liu Huixian, Pan Qihui, Fang Zucheng, Jiang Shengbin, Yang Yucheng. Study on Preparation of UV-Cured Fiber Coatings with Ultra-Low Refractive Index[J]. Paint & Coatings Industry, 2018, 48(1): 44 -47 .
[8] Liu Wei, Su Minchao , Liu Xiaoxuan. Synthesis of Acrylate Resin Modified by Organic Silicon and UV-Curing Kinetics[J]. Paint & Coatings Industry, 2018, 48(1): 48 -53 .
[9] Qi Gang, An Qiufeng, Zhang Qiang. Study on Preparation and Properties of UV-Curable Nano Hybrid Fluorinated Silicone Resin[J]. Paint & Coatings Industry, 2018, 48(1): 54 -58 .
[10] Xu Chunsheng, Wang Tianli, Yao Jinghua, Tao Naiwang, Ren Runtao. Research on Measurement of Barnacle Adhesion Strength in Shear[J]. Paint & Coatings Industry, 2018, 48(1): 59 -62 .
Full text